Material name: 6A02 old name: LD2Standard: GB/T3191-1998
Main features and scope of application:
It has medium strength, high plasticity in annealing and hot state, and plasticity after quenching and natural aging. In this state, the corrosion resistance can be compared with 5A02.3A21, and the artificial aging alloy has a tendency of intergranular corrosion. After quenching , it is not good after annealing. The alloy can be spot welded and hydrogen atom welded, and gas welded.
2, chemical composition
chemical composition:
Silicon Si: 0.50-1.2
Iron Fe: 0.50
Copper Cu: 0.20-0.6
Manganese Mn: 0.15-0.35 or chromium Cr: 0.15-0.35
Magnesium Mg: 0.45-0.9
Zinc Zn: 0.20
Titanium Ti: 0.15
Aluminum Al: balance
other:
Single: 0.05 total: 0.10
Mechanical properties
Tensile strength σb (MPa): ≥ 295
Elongation δ5 (%): ≥12
Note: Longitudinal mechanical properties of bars at room temperature
Specimen size: bar diameter (square bar, hexagonal bar inscribed circle diameter) ≤ 150
Heat treatment specification:
1) Homogenization annealing: heating 525 ~ 540 ° C; holding time is 12 ~ 14h; furnace cooling.
2) rapid annealing: heating 350 ~ 370 ° C; with the effective thickness of the material, heat preservation 30 ~ 120min; air cooling.
3) Quenching and aging: quenching 510 ~ 530 ° C, water cooling; artificial aging 150 ~ 165 ° C, 6 ~ 15h, air cooling; natural aging room temperature 96h.
Status: extruded aluminum and aluminum alloy bars (≤150mm, H112, F.T6)